Stable arc characteristics and good penetration are what you can expect to get from UNIBRAZE 6011 electrode.
Designed for use with AC power sources, UNIBRAZE 6011 has high operator appeal and produces a fine spray
transfer that is ideal for all welding positions. Excellent choice for welding on steels that cannot be completely
cleaned or where the steel is rusty or painted.
APPLICATIONS:
Galvanized steel work, general fabrication, railroad cars, shipbuilding and structural work.
F EATURES : BENEFITS:
• Quick starting • Easy arc striking
• Superior arc drive • Excellent penetration
• Excellent wet-in • Easy weld lay-in and smooth bead appearance
• Slag detaches easily • Quick clean-up
T YPICAL W ELD METAL P ROPERTIES **(Chem Pad):
Weld Metal Analysis AWS Spec (max)
Carbon (C) 0.14 not required
Manganese (Mn) 0.47 not required
Phosphorus (P) 0.009 not required
Sulphur (S) 0.009 not required
Silicon (Si) 0.18 not required
T YPICAL MECHANICAL P ROPERTIES**(AW): AWS Spec (min)
Tensile Strength 77,700 psi (536 MPa) 60,000 psi
Yield Strength 63,200 psi (436 MPa) 48,000 psi
Elongation % in 2” 25% 22%
Reduction of Area 22% to 63% not required
T YPICAL CHARPY -V-NOTCH I MPACT VALUES ** (AW): AWS Spec (min)
Avg at -20°F (-29°C) 30 ft•lbs (41 Joules) 20 ft•lbs
CONFORMANCES AND APPROVALS :
• AWS A5.1, E6011, ASME SFA 5.1, F-3, A-1
• ABS E6011
• CWB E4311
• Lloyd’s Register of Shipping, 2m, 2Ym
Notice: The results reported are based upon testing of the product under controlled laboratory conditions in accordance with American
Welding Society Standards. Actual use of the product may produce different results due to varying conditions. An example of such
conditions would be electrode size, plate chemistry, environment, weldment design, fabrication methods, welding procedure and service
requirements. Thus the results are not guarantees for use in the field. The manufacturer disclaims any warranty of merchantability or
Stable arc characteristics and good penetration are what you can expect to get from UNIBRAZE 6011 electrode.
Designed for use with AC power sources, UNIBRAZE 6011 has high operator appeal and produces a fine spray
transfer that is ideal for all welding positions. Excellent choice for welding on steels that cannot be completely
cleaned or where the steel is rusty or painted.
APPLICATIONS:
Galvanized steel work, general fabrication, railroad cars, shipbuilding and structural work.
F EATURES : BENEFITS:
• Quick starting • Easy arc striking
• Superior arc drive • Excellent penetration
• Excellent wet-in • Easy weld lay-in and smooth bead appearance
• Slag detaches easily • Quick clean-up
T YPICAL W ELD METAL P ROPERTIES **(Chem Pad):
Weld Metal Analysis AWS Spec (max)
Carbon (C) 0.14 not required
Manganese (Mn) 0.47 not required
Phosphorus (P) 0.009 not required
Sulphur (S) 0.009 not required
Silicon (Si) 0.18 not required
T YPICAL MECHANICAL P ROPERTIES**(AW): AWS Spec (min)
Tensile Strength 77,700 psi (536 MPa) 60,000 psi
Yield Strength 63,200 psi (436 MPa) 48,000 psi
Elongation % in 2” 25% 22%
Reduction of Area 22% to 63% not required
T YPICAL CHARPY -V-NOTCH I MPACT VALUES ** (AW): AWS Spec (min)
Avg at -20°F (-29°C) 30 ft•lbs (41 Joules) 20 ft•lbs
CONFORMANCES AND APPROVALS :
• AWS A5.1, E6011, ASME SFA 5.1, F-3, A-1
• ABS E6011
• CWB E4311
• Lloyd’s Register of Shipping, 2m, 2Ym
Notice: The results reported are based upon testing of the product under controlled laboratory conditions in accordance with American
Welding Society Standards. Actual use of the product may produce different results due to varying conditions. An example of such
conditions would be electrode size, plate chemistry, environment, weldment design, fabrication methods, welding procedure and service
requirements. Thus the results are not guarantees for use in the field. The manufacturer disclaims any warranty of merchantability or
fitness for any particular purpose with respect to its product
RECOMMENDED W ELDING PROCEDURES :
G ENERAL: AC or electrode positive work, negative (DCEP)
A RC LENGTH: Average length (1/8” to 1/4”)
FLAT: Stay ahead of puddle and use slight whipping motion
VERTICAL-U P : Use slight whipping or weaving technique
VERTICAL-D OWN: Use higher amperage and faster travel, staying ahead of the puddle
O VERHEAD : Stay ahead of puddle and use slight whipping motion
STORAGE : Dry at room temperature, humidity below 50% should be avoided;
at no time should this electrode be stored in an oven above 130°F
R ECONDITIONING: Not recommended
Notice: The results reported are based upon testing of the product.
G ENERAL: AC or electrode positive work, negative (DCEP)
A RC LENGTH: Average length (1/8” to 1/4”)
FLAT: Stay ahead of puddle and use slight whipping motion
VERTICAL-U P : Use slight whipping or weaving technique
VERTICAL-D OWN: Use higher amperage and faster travel, staying ahead of the puddle
O VERHEAD : Stay ahead of puddle and use slight whipping motion
STORAGE : Dry at room temperature, humidity below 50% should be avoided;
at no time should this electrode be stored in an oven above 130°F
R ECONDITIONING: Not recommended
Notice: The results reported are based upon testing of the product.
There are no reviews yet so why don't you use the form here and be the first to submit a review?
Related Items
More Related Items
Less Related Items